Modification of Montmorillonite with Cetyl Trimethylammonium Bromide and Tetra Ethyl Ortho Silicate

Modification of montmorillonite (MMt) with cetyltrimethylammonium bromide (CTAB) and tetraethyl ortosilicate (TEOS) has been done. The aim of the research is to study the effect of TEOS and CTAB into MMt. This research is a preliminary step to invent material that can be modified with other functional materials. The study was conducted by recting TEOS with MMt and varying CTAB concentration on MMt previously modified with TEOS. The TEOS concentration was 4.72 M while CTAB concentration was 0.25; 0.5; 2; 3.5; and 5 mmol/g in MMt which has been reacted with TEOS. Material characterization was done by X-Ray Diffraction (XRD), Fourrier Transform Infra-Red Spectrophotometer (FTIR) and Scanning Electron Microscope (SEM). Cation exchange capacity (CEC) of materials was analyzed by titration method. The results show that TEOS and CTAB successfully modified. TEOS adsorbed onto MMt. It was identified from increased basal spacing, specific group and also by its elemental composition, originally having basal spacing 16 Å. After modification with CTAB, basal spacing increased to 28.45 Å or 77.64%. This indicates that CTAB is intercalated within the MMt layers. The CEC of new material is 0.93 meq/g, increase from 0.83 meq/g. (paper)