Magneto-resistance of NiFe nanowire with zigzag shape

The anisotropic magneto-resistance (AMR) contributions of a zigzag-shaped NiFe wire were investigated. The magneto-resistance (MR) behaviors in different magnetic-field directions clearly reflect the angular relationships between the directions of the current and magnetic moment in the subdivisions. The resistance in remanence after magnetization along 0o in respect to the longer direction of zigzag was larger than that along 90o. Assumed that the difference appears due to the AMR contribution in the domain wall trapped at the corner, the MR ratio was estimated to be 1.2%, which is in good agreement with the AMR of the NiFe film. We clearly showed that the domain-wall resistance originates in the AMR.