Roles of Hydrogen and Plastic Strain Distribution on Delayed Crack Growth in Single-crystalline Fe–Si alloy

  • 1. Graduate School of Engineering, Kyushu University, 744 Motooka, Nishi-ku, Fukuoka, 819-0395 (Japan)
  • 2. Department of Mechanical Engineering, Can Tho University, Campus II, Ninh Kieu District, Can Tho (Viet Nam)
  • 3. Department of Mechanical Engineering, Kyushu University, 744 Motooka, Nishi-ku, Fukuoka, 819-0395 (Japan)
  • 4. Elements Strategy Initiative for Structural Materials (ESISM), Kyoto University, Yoshidahonmachi, Sakyo-ku, Kyoto, 606-8501 (Japan)
  • 5. Research Center for Structural Materials, National Institute for Materials Science, 1-2-1 Sengen, Tsukuba, 305-0047 (Japan)

Description

Highlights: • Roles of hydrogen and plastic strain distribution on delayed crack growth. • Effect of hydrogen on macroscopic and microscopic features of crack growth. • Hydrogen-enhanced localized plasticity (HELP) is relevant to plastic strain gradients. • Reverse plastic strain enlarges crack tip opening angle (CTOA) and blunts crack tip. • Roles of Hydrogen and Plastic Strain Distribution on Delayed Crack Growth in Single-Crystalline Fe–Si Alloy. Effects of hydrogen on macroscopic and microscopic features of crack growth in thin specimens were investigated using a thin sheet of single-crystal Fe-3wt%Si alloy. Center-cracked specimens were tested under a sustained load in a hydrogen environment, and under continuous stretching in an air environment. The fracture features were compared to elucidate the role of hydrogen in hydrogen-induced delayed crack growth. In both air and hydrogen environments, the crack growth mode of the thin specimens was the same as that of the thick specimens, despite the significantly reduced thickness. Surprisingly, the crack grew discontinuously, and left striations on the fracture surface, in which shorter striation spacing was observed in hydrogen. In addition, there was a similarity in the deformation microstructures beneath the fracture surface, that is, both microstructures were composed of three distinct layers characterized by different plastic strain gradients and dislocation densities. In the hydrogen environment, the hydrogen-enhanced localized plasticity (HELP) mechanism is believed to be relevant to the crack growth process. Also, HELP was supposed to cause different characteristics (the magnitude of plastic strain, the plastic strain gradient, and dislocation structure) of the three layers in the hydrogen compared to those in the air. Reverse plastic deformation occurred in the regions behind the crack front during crack growth, which is speculated to contribute not only to enlarge the crack tip opening angle (CTOA) but also to blunt the crack tip.

Availability note (English)

Available from http://dx.doi.org/10.1016/j.msea.2020.140703

Additional details

Identifiers

DOI
10.1016/j.msea.2020.140703;
PII
S0921509320317664;

Publishing Information

Journal Title
Materials Science and Engineering. A, Structural Materials: Properties, Microstructure and Processing
Journal Volume
803
Journal Page Range
vp.
ISSN
0921-5093
CODEN
MSAPE3

Optional Information

Copyright
Copyright (c) 2020 Elsevier B.V. All rights reserved.