Characterization of ZnO Nanoparticles using Superconducting Tunnel Junction Cryodetection Mass Spectrometry

Zinc oxide (ZnO) nanoparticles coated with either n-octylamine (OA) or α-amino poly(styrene-co-acrylonitrile) (PSAN) ligands (L) have been analyzed using laser desorption/ionization and matrix assisted laser desorption/ionization (MALDI) time-of-flight (TOF) superconducting tunnel junction (STJ) cryodetection mass spectrometry. STJ cryodetection has the advantage of high m/z detection and allows for the determination of average molecular weights and dispersities for 500–600 kDa ZnO-L nanoparticles. The ability to detect the relative energies deposited into the STJs has allowed for investigation of ZnO-L metastable fragmentation. ZnO-L precursor ions gain enough internal energy during the MALDI process to undergo metastable fragmentation in the flight tube. These fragments produced a lower energy peak, which was assigned as ligand-stripped ZnO cores whereas the individual ligands were at too low of an energy to be observed. From these STJ energy resolved peaks, the average weight percentage of inorganic material making up the nanoparticle was determined, where ZnO-OA and ZnO-PSAN nanoparticles are comprised of ~62% and ~68% wt ZnO, respectively. In one example, grafting densities were calculated based on the metastable fragmentation of ligands from the core to be 16 and 1.1 nm^–2 for ZnO-OA and ZnO-PSAN, respectively, and compared with values determined by thermogravimetric analysis (TGA) and transmission electron microscopy (TEM). .