Modification of nylon-6 with semi-rigid poly (p-diphenyl oxide terephthalamide)

In this study, the flexible nylon-6 was reinforced by the semi-rigid aromatic polyamide, poly (p-diphenyl oxide terephthalamide) (POA), through physical polybending and chemical copolymerization using p-aminophenylacetic acid (P-APA) as a coupling agent. From the DSC measurements, it was shown that Tg of the polyblends was increased with the increase of POA content. The Tg and Tm of multiblock copolyamides were found to be higher than those of polyblends and triblock copolyamides. From the Rheovibron measurements, it was shown that the POA with nylon-6 poy-blends exhibited higher E' and Tg value than that of nylon-6, which increased with the increase of POA content. The Tg and E' values of multiblock copolyamides were higher than those of polyblends triblock copolyamides. Scanning electron microscopy revealed that the polyblends were a dispersed phase structure, although the multiblock copolyamides exhibited a homogeneous texture rather than an aggregated one. From the wide-angle x-ray diffraction pattern, the triblock copolyamides and polyblends had two diffraction peaks, i.e., 2 θ = 20.5 degrees and 24 degrees. However, the multiblock had only one at 2 θ = 20 degrees, which indicates that a different crystal structure of multiblock copolyamides. For the mechanical properties, it was found that the multiblock copolyamides had a more significant reinforcing effect than those of polyblends and triblock copolyamides. 21 refs., 11 figs., 5 tabs