SAP-like ultrafine-grained Al composites dispersion strengthened with nanometric AlN

This paper reports the development of novel Sinter-Aluminum-Pulver (SAP)-like Al–AlN nanocomposites via replacing the native Al2O3 thin films on fine Al powder with a large volume fraction of in situ formed nanometric AlN dispersoids. Fine gas-atomized Al powder (d50=1.3 µm) compacts were first partially nitrided at 590 °C in flowing nitrogen, controlled by a small addition of Sn (0.3–0.4 wt%), and subsequently consolidated by hot direct extrusion. The resulting Al–AlN composites consisted of submicrometric Al grains reinforced with nanometric AlN dispersoids together with some nanometric Al2O3 dispersoids. An Al–13 vol% AlN nanocomposite fabricated this way achieved exceptional ultimate tensile strength of 227 MPa, yield strength of 195 MPa and Young's modulus of 66 GPa at 300 °C, superior to typical SAP materials and coarse grained Al–AlN composites. In addition, the Al–13 vol% AlN nanocomposite exhibited good thermal stability up to 500 °C. The strengthening mechanism is discussed