Low-temperature plasticity of electron irradiated Kh18N10T stee;
Description
The Kh18N10T steel has been studied for irradiation effect on the character of low-temperature deformation curves. It is shown that after electron irradiation the steel low-temperature dictility gets gher due to an increase in the extent of a stable austenite existence iection reflected in the extension diagrams. It is supposed that the revealed phenomenon may be attributed to an increase of the stacking fault energy in the irradiated steel
Additional details
Additional titles
- Original title (Russian)
- Низкотемпературная пластичност' стали Kh18N10T, облученной электронами
Publishing Information
- Journal Title
- Probl. Prochn.
- Journal Issue
- no.1
- Series
- Probl. Prochn.
- ISSN
- 0556-171X
INIS
- Country of Publication
- Ukraine
- Country of Input or Organization
- USSR
- INIS RN
- 13688894
- Subject category
- S36: MATERIALS SCIENCE;
- Descriptors DEI
- CRYSTAL-PHASE TRANSFORMATIONS; ELECTRONS; LOW TEMPERATURE; MEV RANGE 100-1000; PHYSICAL RADIATION EFFECTS; PLASTICITY; S-N DIAGRAM; SLIP; STACKING FAULTS; STEEL-KH18N10T; STRAIN HARDENING; TENSILE PROPERTIES
- Descriptors DEC
- ALLOYS; CARBON ADDITIONS; CHROMIUM ALLOYS; CHROMIUM STEELS; CHROMIUM-NICKEL STEELS; CORROSION RESISTANT ALLOYS; CRYSTAL DEFECTS; CRYSTAL STRUCTURE; DIAGRAMS; ELEMENTARY PARTICLES; ENERGY RANGE; FERMIONS; HARDENING; INFORMATION; IRON ALLOYS; IRON BASE ALLOYS; LEPTONS; MANGANESE ALLOYS; MECHANICAL PROPERTIES; MEV RANGE; NICKEL ALLOYS; PHASE TRANSFORMATIONS; RADIATION EFFECTS; STAINLESS STEELS; STEELS; TITANIUM ADDITIONS; TRANSITION ELEMENT ALLOYS
Optional Information
- Notes
- For English translation see the journal Strength of Materials (USA).