Grafting of styrene into pre-irradiated fluoropolymer films: Influence of base material and irradiation temperature

In this study, the influence of irradiation temperature on mechanical properties of three fluoropolymers and on grafting of styrene into the polymers by the pre-irradiation method was investigated. Electron paramagnetic resonance spectroscopy and infrared spectroscopy were used to characterize the irradiated polymers regarding trapped radical species and changes in the chemical structure, respectively. For poly(tetrafluoroethylene-co-perfluoropropyl vinyl ether) (PFA) the irradiation temperature was found to be an important factor for tensile strength and elongation at break of the pre-irradiated film. No strong effect of irradiation temperature on the mechanical properties was noticed for poly(tetrafluoroethylene-co-ethylene) (ETFE); however the yield of grafting drops at high irradiation temperatures. Finally, mechanical properties of poly(tetrafluoroethylene) (PTFE) were found to be dramatically altered, even if the film was irradiated at elevated temperature.