Evolution process of the synthesis of TiC in the Cu-Ti-C system

The evolution process of TiC formation in the 20 wt.% Cu-Ti-C powder mixtures was studied by using differential thermal analysis (DTA), X-ray diffraction (XRD) and scanning electron microscopy (SEM). The TixCuy compounds (Ti2Cu, TiCu, Ti3Cu4 and TiCu4) formed initially via solid-state diffusion reactions between Cu and Ti particles; and then Ti2Cu and TiCu can form a Cu-Ti eutectic liquids at about 1233 K. The unreacted Ti and C particles dissolved into the Cu-Ti liquids and led to the formation of Cu-Ti-C ternary liquids; subsequently, TiC particulates precipitated out of the saturated liquids. At the same time, also the formation of Ti2Cu occurred at the interface between the Cu-Ti liquids and the unreacted Ti particles. As the temperature increased further, the Ti2Cu melted and more Cu-Ti liquids formed; and then C particles continuously dissolved into the Cu-Ti-C liquids and TiC particulates gradually precipitated out of the saturated liquids