Significance of the state of segregation of the carbide phase on the toughness properties of 20 MnMoNi 5 5 forgings
Creators
- 1. Thyssen Henrichshuette A.G., Hattingen (Germany, F.R.)
Description
When measured in the heat treated wall thickness of heavy forgings, 20 Mn Mo Ni 5 5 steel is so low in allow that it is unavoidable that large parts of higher bainite will occur in the structure of the pieces. In order to obtain the best possible notch impact strength values, tempering is of particular importance. It must be done so that there is the least possible segregation of molybdenum carbide Mo2C in the bainite ferrite. This requires the use of not too high tempering temperatures together with an upper limit of tempering time. Similar considerations apply for stress relieving treatment. (orig.)
Abstract (German)
Gemessen an den bei schweren Schmiedestuecken vorliegenden Verguetungswanddicken ist der Stahl 20 MnMoNi 5 5 so niedrig legiert, dass es unvermeidlich ist, grosse Anteile an oberem Bainit im Gefuege der Stuecke einzustellen. Um bestmoegliche Kerbschlagarbeitswerte zu erzielen, kommt der Anlassbehandlung besondere Bedeutung zu. Sie muss so gefuehrt werden, dass es im bainitischen Ferrit in moeglichst geringem Masse zur zaehigkeitsmindernden Ausscheidung von Molybdaen-Karbid Mo2C kommt. Dazu ist die Anwendung nicht zu hoher Anlasstemperaturen in Verbindung mit einer nach oben begrenzten Anlasszeit erforderlich. Entsprechende Ueberlegungen gelten fuer das Spannungsarmgluehen. (orig.)Additional details
Additional titles
- Original title (German)
- Bedeutung des Ausscheidungszustandes der Karbidphasen auf die Zaehigkeitseigenschaften von Schmiedestuecken aus dem Stahl 20 MnMoNi 5 5
Publishing Information
- Imprint Title
- Fracture prevention and availability in the series safety of the pressure boundary of light water reactors. Materials for advanced reactor systems
- Imprint Pagination
- 506 p.
- Journal Page Range
- vp.
- Report number
- INIS-mf--8881
Conference
- Title
- 9. MPA seminar on fracture prevention and availability.
- Dates
- 13-14 Oct 1983.
- Place
- Stuttgart (Germany, F.R.).
INIS
- Country of Publication
- Germany
- Country of Input or Organization
- Germany
- INIS RN
- 15046096
- Subject category
- S36: MATERIALS SCIENCE;
- Resource subtype / Literary indicator
- Conference
- Descriptors DEI
- CARBIDES; FORGING; FRACTURE PROPERTIES; HEAT TREATMENTS; NOTCHES; SEGREGATION; STEEL-MNNIMO
- Descriptors DEC
- ALLOYS; CARBON ADDITIONS; CARBON COMPOUNDS; FABRICATION; IRON ALLOYS; IRON BASE ALLOYS; LOW ALLOY STEELS; MANGANESE ALLOYS; MATERIALS WORKING; MECHANICAL PROPERTIES; MOLYBDENUM ADDITIONS; NICKEL ADDITIONS; STEELS
Optional Information
- Notes
- Imprint:Bruchsicherheit und Verfuegbarkeit aus der Reihe Sicherheit der druckfuehrenden Umschliessung von Leichtwasserreaktoren in Verbindung mit Werkstoffeinsatz fuer fortgeschrittene Reaktorsysteme.