Stability of A-15 compounds in multifilamentary superconducting wires

With the pre-eminence of A-15 superconducting multifilamentary wires in magnet technology, it has become important to understand the thermodynamic factors influencing the formation of these compounds under solid-state reaction conditions. The six systems Nb--Sn, Nb--Ga, Nb--Ge, Nb--Al, V--Si, and V-Ga were prepared as single-filament bronze wires and heat treated in an attempt to precipitate the appropriate A-15 compound. The compounds observed to form were categorized using a formation temperature ratio (stability index) based on the melting temperatures of the constituents which make up the single filament composites. This study has led to several predictions regarding the formation of A-15 compounds using a solid-state bronze diffusion technique. Results of experimentation based on these predictions are presented. (auth)