Separation of actinides and lanthanides from acidic nuclear wastes by supported liquid membranes

Supported liquid membranes, SLM, consisting of a solution of 0.25 M octyl(phenyl)-N,N-diisobutylcarbamoylmethylphosphine oxide (CMPO) and 0.75 M tributylphosphate (TBP) in decalin absorbed on thin microporous polypropylene supports, have been studied for their ability to perform selective separations and concentrations of actinide and lanthanide ions from synthetic acidic nuclear wastes. The permeability coefficients of selected actinides (Am, Pu, U, Np) and of some of the other major components of the wastes have been measured using SLMs in flat-sheet and hollow-fiber configurations. The results have shown that with the thin (25 μm) flat-sheet SLMs, using Celgard 2500 as support, the membrane permeation process is mainly controlled by the rate of diffusion through the aqueous boundary layers. With the thicker (430 μm) hollow-fiber SLMs, using Accurel hollow-fibers as support, the membrane permeation process is controlled by the rate of diffusion through both the SLM and the aqueous boundary layers. Hollow-fibers SLMs exhibited lower permeability coefficients and longer life-times. The experiments have shown that the actinides can be very efficiently removed from the synthetic waste solutions to the point that the resulting solution could be considered a non-transuranic waste (less than 100 mCi/g of disposed form). The work has demonstrated that actinide removal from synthetic waste solutions is a feasible chemical process at the laboratory scale level