Sorptive properties of antimony-doped In2O3

Creators

  • 1. RAN, Inst. Problem Khimicheskoj Fiziki, Chernogolovka (Russian Federation)

Description

Chemisorption of O2, Cl2, and SO2 on the surface of nanocrystalline In2O3 doped with antimony (0.2 and 2.7 at %) has been studied at temperatures from 22 to 200 deg C. The results indicate that antimony prevents the formation of nonconducting indium chlorides on the surface of nanocrystalline In2O3 during Cl2 chemisorption. The logarithm of the conductivity of Sb-doped In2O3 is a nearly linear function of the surface coverage with chlorine, which makes it a candidate chlorine-sensing material. At the same time, antimony doping reduces the SO2 response of In2O3

Abstract (Russian)

Исследована хемосорбция О2, Сl2 и SO2 на поверхности нанокристаллического In2O3, содержащего добавку сурьмы (0.2 и 2.7 ат. %) при температурах 22-200 град С. Установлено, что в процессе хемосорбции Сl2 добавка сурьмы препятствует образованию непроводящих хлоридов индия на поверхности нанокристаллического In2O3. Между заполнением поверхности модифицированных образцов хлором и логарифмом изменения электропроводности наблюдается зависимость, близкая к линейной, что делает данный материал перспективным для использования в качестве полупроводникового сенсора на хлор. Чувствительность модифицированного In2О3 по отношению к SO2 снижается

Additional details

Additional titles

Original title (Russian)
Сорбционные свойства модифицированного сурьмой Ин

Publishing Information

Journal Title
Neorganicheskie Materialy
Journal Volume
43
Journal Issue
10
Journal Page Range
p. 1211-1218
ISSN
0002-337X
CODEN
NEOMB8

INIS

Country of Publication
Russian Federation
Country of Input or Organization
Russian Federation
INIS RN
39052394
Subject category
S37: INORGANIC, ORGANIC, PHYSICAL AND ANALYTICAL CHEMISTRY;
Descriptors DEI
ANTIMONY COMPOUNDS; CHEMICAL REACTION KINETICS; CHEMISORPTION; CHLORINE; CRYSTALS; DOPED MATERIALS; ELECTRIC CONDUCTIVITY; INDIUM OXIDES; OXYGEN; PARTICLE SIZE; SORPTIVE PROPERTIES; SULFUR DIOXIDE; TEMPERATURE DEPENDENCE; TEMPERATURE RANGE 0273-0400 K; TEMPERATURE RANGE 0400-1000 K
Descriptors DEC
CHALCOGENIDES; CHEMICAL REACTIONS; ELECTRICAL PROPERTIES; ELEMENTS; HALOGENS; INDIUM COMPOUNDS; KINETICS; MATERIALS; NONMETALS; OXIDES; OXYGEN COMPOUNDS; PHYSICAL PROPERTIES; REACTION KINETICS; SEPARATION PROCESSES; SIZE; SORPTION; SULFUR COMPOUNDS; SULFUR OXIDES; SURFACE PROPERTIES; TEMPERATURE RANGE

Optional Information

Notes
18 refs., 7 figs., 1 tab.