Development of Superhydrophobic Material SS 17-4 PH for Bracket Orthodontic Application by Metal Injection Molding

Dental's plaque is a common problem that encountered during orthodontic treatment using bracket. It is caused by demineralization of enamel due to the activity of bacteria. The bacteria increase with remaining excess food which trapped in teeth and bracket. A hydrophobic surface could reduce food attachment on the bracket because of extremely low wettability properties that make it easy to clean with water. There are several methods to obtain hydrophobic surfaces, which are sol-gel, template replica and also etching. The propose of this work is to compare etching treatment and surface modification on sintered SS 17-4 PH as bracket material using CuCl₂ and HCl as an etchant while stearic acid was used for surface modification. Hydrophobic surfaces were produced under various etching time i.e 15, 30, 45 and 60 seconds for CuCl₂ and 40, 50, 60 and 70 minutes for HCl and also HCl concentration i.e 1,2 and 3 mol/L at room temperature. The hydrophobicity is observed using contact angle measurement while the microstructures observed by Scanning Electron Microscope. The result shows the contact angle could be achieved up to 60% higher than the as-sintered material. Hydrophobic structure has successfully fabricated using etching technique that might be applied to the orthodontic bracket. (paper)