Effects of rare-earths additions on the breakdown of protective oxide scales in the presence of sulfur

Minor additions of rare-earths improve oxide scale adhesion in simple oxidation at high temperatures. The efficacy of such improvements and the role of such additions are not well understood in the presence of sulfur at 500-700 degrees C. Therefore, mixed gas corrosion tests were performed on model Fe-based alloys, with minor additions of rare-earths in an H2/H2S/H2O/Ar gas mixture at 700 degrees C up to 192 hours. The scale breakdown mechanisms were studied on preoxidized samples. The scales and the substrates were characterized by SEM/EDS, and scanning Auger microscopy (AES). The results are discussed