Powder-technological vitrification of HAW from LWR and FBR reprocessing
Creators
- 1. Kernforschungszentrum Karlsruhe G.m.b.H. (Germany, F.R.). Inst. fuer Material- und Festkoerperforschung
Description
Whereas (simulated) HLW is denitrified first, (simulated) FKS is directly mixed with glas frit and dryed in oil heated mixers. After calcination within the highgrade steel mould at a temperature of 850 or 950 K (depending on the type of glass and waste), the mixture is sintered for several hours under pressures between 0.4 and 1.0 MPa and at temperatures of 920 or 1020 K. The low process temperature and the prevention of the liquid phase result in (I) the reduction of the waste steam loss, (II) the prevention of segregations and problems with corrosions, (III) the reduction of the dependency of the product properties on the changes in the waste composition and loading, (IV) the possible use of higher-melting glasses of higher leaching resistance. The procedure has been demonstrated inactively for diameters of up to 30 cm; for the application in hot operation adaption measures may be required. (orig.)
Abstract (German)
Waehrend (simulierter) HLW zunaechst denitriert wird, wird (simulierter) FKS direkt mit Glasfritte gemischt und in einem oelbeheizten Mischer getrocknet. Nach Kalzinierung innerhalb der Edelstahlkokille bei 850 bzw. 950 K (je nach Glas- und Abfallart), wird die Mischung mehrere Stunden bei 920 bzw. 1020 K und Druecken zwischen 0,4 und 1,0 MPa druckgesintert. Durch die niedrige Prozesstemperatur und die Vermeidung des fluessigen Zustandes werden (I) die Abdampfverluste gesenkt, (II) Segregationen und Korrosionsprobleme vermieden, (III) die Abhaengigkeit der Produkteigenschaften von Veraenderungen der Abfallzusammensetzung und -beladung reduziert, (IV) die Verwendung von hoeherschmelzenden Glaeser mit hoeherer Auslaugbestaendigkeit ermoeglicht. Das Verfahren ist bisher inaktiv bis zu 30 cm Durchmesser demonstriert; zur Anwendung im heissen Betrieb sind ggf. noch Anpassungsmassnahmen erforderlich. (orig.)Additional details
Additional titles
- Original title (German)
- Pulvertechnologische Verglasung von hochradioaktivem Abfall aus der LWR- und SBR-Wiederaufarbeitung
Publishing Information
- Imprint Title
- Papers presented at the 7th status report of the Reprocessing and Waste Treatment Project
- Imprint Pagination
- 463 p.
- Journal Page Range
- p. 453-463.
- Report number
- KFK--4476
Conference
- Title
- 7. status report of the Reprocessing and Waste Treatment Project of Kernforschungszentrum Karlsruhe GmbH.
- Original Conference Title
- 7. Statusbericht des Projekts Wiederaufarbeitung und Abfallbehandlung (PWA) des Kernforschungszentrums Karlsruhe GmbH
- Dates
- 15-16 Mar 1988.
- Place
- Karlsruhe (Germany, F.R.).
INIS
- Country of Publication
- Germany
- Country of Input or Organization
- Germany
- INIS RN
- 20066313
- Subject category
- S12: MANAGEMENT OF RADIOACTIVE WASTES, AND NON-RADIOACTIVE WASTES FROM NUCLEAR FACILITIES;
- Resource subtype / Literary indicator
- Conference
- Descriptors DEI
- BENCH-SCALE EXPERIMENTS; CHEMICAL COMPOSITION; COMPACTING; FISSION PRODUCTS; GLASS; HIGH-LEVEL RADIOACTIVE WASTES; LEACHING; MICROSTRUCTURE; POWDER METALLURGY; RESIDUES; SIMULATION; SINTERED MATERIALS; SINTERING; SLURRIES; VITRIFICATION; WASTE FORMS
- Descriptors DEC
- CRYSTAL STRUCTURE; DISPERSIONS; DISSOLUTION; FABRICATION; ISOTOPES; MATERIALS; METALLURGY; MIXTURES; RADIOACTIVE MATERIALS; RADIOACTIVE WASTES; SEPARATION PROCESSES; SUSPENSIONS; WASTES
Optional Information
- Notes
- Imprint:Sammlung der Vortraege anlaesslich des 7. Statusberichtes des Projektes Wiederaufarbeitung und Abfallbehandlung.
- Secondary number(s)
- PWA--44/88.