Martensitic transformation and trip-effect in Fe-Ni-Mn alloys upon low-temperature deformation

Creators

  • 1. Tsentral'nyj Nauchno-Issledovatel'skij Inst. Chernoj Metallurgii im. I.P. Bardina, Moscow (Russian Federation)

Description

Experimental study of martensitic transformation at 77 K is carried out in a set of Fe-Ni-Mn alloys with a nickel content of 22.65 - 22.9 wt. % and a manganese content ranging within 3.34 - 6.05 wt. %. It is revealed that deformation below the temperature of the completion of spontaneous transformation results in intense transformation accompanied by a plasticity increase. The amount of martensite arising in the process of low temperature deformation grows with a decrease of manganese concentration in the alloy. The factors determining the intensity of martensitic transformation and alloys properties on low temperature deformation are discussed

Abstract (Russian)

Экспериментально изучено мартенситное превращение при 77 К в серии сплавов Fe-Ni-Mn с содержанием никеля 22.65 - 22.9 вес. % и марганца в диапазоне 3.34 - 6.05 вес. %. Установлено, что деформация при температуре ниже температуры конца спонтанного превращения приводит к интенсивному превращению, сопровождающемуся повышением пластичности. Количество образующегося в процессе низкотемпературной деформации мартенсита увеличивается при уменьшении содержания в сплаве марганца. Обсуждены факторы, определяющие интенсивность мартенситного превращения и свойства сплавов при низкотемпературной деформации

Additional details

Additional titles

Original title (Russian)
Мартенситное превращение и трип-эффект в сплавах Фе-Ни-Мн при низкотемпературной деформации

Publishing Information

Journal Title
Fizika Metallov i Metallovedenie
Journal Volume
100
Journal Issue
3
Journal Page Range
p. 91-94
ISSN
0015-3230
CODEN
FMMEA9

INIS

Country of Publication
Russian Federation
Country of Input or Organization
Russian Federation
INIS RN
37020044
Subject category
S36: MATERIALS SCIENCE;
Descriptors DEI
CARBON ADDITIONS; COLD WORKING; CONCENTRATION RATIO; CRYSTAL-PHASE TRANSFORMATIONS; DUCTILITY; IRON BASE ALLOYS; MANGANESE ALLOYS; MARTENSITE; METALLURGICAL EFFECTS; NICKEL ALLOYS; STRAINS; STRESSES; TENSILE PROPERTIES
Descriptors DEC
ALLOYS; CARBON ADDITIONS; DIMENSIONLESS NUMBERS; FABRICATION; IRON ALLOYS; MATERIALS WORKING; MECHANICAL PROPERTIES; PHASE TRANSFORMATIONS; TENSILE PROPERTIES; TRANSITION ELEMENT ALLOYS

Optional Information

Notes
14 refs., 6 figs., 1 tab.