Layered double hydroxide nanosheet as a two-dimensional support of dense platinum nanoparticles

Transition metal nanoparticles (NPs) with a narrow size distribution have been intensively synthesized on various solid supports for anti-agglomeration, and high catalytic activity and selectivity. Layered double hydroxides (LDH) are currently attracting intense interest in the field of heterogeneous catalysis as catalyst supports. In order to obtain a well-crystallized LDH nanosheet, the as-synthesize d carbonate form of LDH was hydrothermally treated according to a reported procedure, and further reacted by anion-exchange with an aqueous solution of NaNO₃ and acetate buffer to give the nitrate form of LDH. Dense and uniform Pt NPs were synthesized on the exfoliated LDH nanosheets through precursor exchange and thermal reduction of the precursor ions. In this nanocomposite, the Pt Nps were uniformly grown on the surface of the LDH nano sheet and the average size of Pt Nps was 2nm