Electrochemical corrosion behavior of A 516 steel using corrosive environments with varying concentrations of sodium thiosulphate

The corrosion behavior of A 516 steel was studied by potentiodynamic polarization technique. Environment used for these tests was sodium chloride (5%), acetic acid (0.5%) and sodium thiosulphate with varying concentration from 0.001 M to 1 M. Surface study was also carried out using optical microscope. The potentiodynamic polarization results revealed the formation of large number of pits in the sample, which was tested in the solution containing NaCl. Pitting corrosion study of alloy A516 G-70 was also conducted to see the effect of different concentrations of thiosulfate with or without addition of NaCl and acetic acid at room temperature. It was observed that different thiosulfate concentrations did not produce any difference in the polarization behavior of the alloys, when added in 5% NaCl and 0.5% acetic acid solution. However, in the absence of NaCl and acetic acid, thiosulfate concentration 0.001 mol/l or higher did produce general corrosion and pitting in the alloy at room temperature is shown.(Orig./A.B.)