The kinetics of titanium leaching of ilmenite using HCl

The research of ilmenite leaching of tailings processing zircon sand has been done. Tailings of processing zircon sand contain Zr, Ti, Nb and Fe. Determination of leaching kinetics of Ti on ilmenite using HCl was done on this research. Determination of reaction rate consist the influence of weight ratio of HCl to ilmenite, HCl molarity and temperature reaction. The experiment of kinetics was done by varying the temperature reaction from 70°C to 108°C and time parameter range 0 to 200 minutes. From data of research can be concluded that the greater of weight ratio of HCl with ilmenite, M HCl and reaction temperature, the faster rate of reaction. On weight ratio of HCl with ilmenite varied 4 - 20, average reaction rate along 50 minutes and instantaneous reaction rate in the first 50 minutes ranged from 0.0021 to 0.0032 gmol/(l.minute). Average reaction rate along 250 minutes ranged from 0.0005 to 0.0007 gmol/(l.minute) and instantaneous reaction rate at 50 minutes latest ranged from 0.0000 to 0.0001 gmol/(l.minute). For M HCl = 8 to 12.23 M, average reaction rate and instantaneous reaction rate in the first 50 minutes ranged from 0.0012 to 0.0026 gmol/(l.minute). Average reaction rate along 250 minutes ranged from 0.0004 to 0.0006 gmol/(l.minute) and instantaneous reaction rate at 50 minutes latest ranged from 0.0000 to 0.0001 gmol/(l.minute). On reaction temperature = 70 - 108°C, average reaction rate along 50 minutes and instantaneous reaction rate in the first 50 minutes ranged from 0.0012 to 0.0032 gmol/(l.minute). Average reaction rate along 250 minutes ranged from 0.0002 to 0.0006 gmol/(l.minute) and instantaneous reaction rate at 50 minutes latest ranged from 0.0000 to 0.0001 gmol/(l.minute). The leaching reaction of Ti in ilmenite was second order reaction. The relationship between temperature (T) with the reaction rate constant (k) are - ln k = 3333.2/T - 1.3685 or k = 1.3685.^e-3333,2/T, frequency factor A = 1446 and activation energy E = 27.712 kJ/mol. (author)