Dispersant Application during SG Wet Layup at SK Unit 1

The corrosion products in the feedwater are deposited onto the steam generators (SGs) despite the effort to control them within limit of impurity. This deposit is one of causes for occurrence of SCC (Stress Corrosion Cracking), water level fluctuation and further corrosion of SGs. To minimize corrosion and remove deposit, the nuclear power plants apply high pH to the secondary system and SG chemical cleaning, respectively. But these methods can be costly and carry risks of extended outages or incomplete cleaning. Another method is an on-line dispersant application. The role of dispersant is to make deposit suspended in the SGs. Then, the suspended deposit is discharged to the blowdown system. The iron removal is increased in the blowdown system during the dispersant application. Additional significant benefit in the form of reduced corrosion product transport may be obtained through applying dispersant in the SGs wet lay operational mode. This method helps to reduce the total SGs loading without affecting critical outage activities and with minimal additional effort on the part of the utilities. This study provides the results of the dispersant application trial during the SG wet layup at SK Unit 1. As the PAA concentrations were increased, the corrosion rates of Alloy 690 and SA 106 Gr.B were increased. The corrosion rate of Alloy 690 was 2 times less than that of SA 106 Gr.B at 100 ppm of PAA based on the electrochemical experimental. There were no significant feasibility problems with application of PAA during the SG wet layup. The reasonable estimation of the additional mass removed by the presence of PAA during SGs wet layup is 460 g. The iron removal depended on PAA concentration injected based on the comparative results of the SK Unit 1 and TMI-1. It is expected that injection of PAA into the SG result in a significant decrease in the amount of iron transported to the SGs during the startup