Model for gaseous porosity evolution under postradiation annealing of BCC and FCC materials irradiated with He ions
- 1. Moskovskij Inzhenerno-Fizicheskij Inst. (Gosudarstvennyj Univ.), Moscow (Russian Federation)
Description
Specific features of helium porosity formation on post-irradiation annealing (600-750 deg C for 1 and 5 h) are analyzed for BCC and FCC lattice materials (high-alloy steels, nickel base alloys, V-Ti alloys) implanted with helium ions at room temperature. Higher binding energy of helium-vacancy complexes in BCC metals is shown to repress the evolution of gaseous porosity. The formation of complicated complexes of HemMekVn in the alloys with substitutional alloying elements which are more thermally stable than simple complexes of HemVn type in unalloyed metals induces the formation of smaller bubbles and lower gaseous swelling in alloys
Abstract (Russian)
Рассмотрены особенности формирования гелиевой пористости при послерадиационных отжигах (600-750 град С в течение 1 и 5 ч) в ОЦК и ГЦК материалах, имплантированных гелием при комнатной температуре. Показано, что более высокая энергия связи гелий-вакансионных комплексов в ОЦК металлах подавляет развитие газовой пористости. Образование в сплавах сложных комплексов типа HemMekVn с элементами замещения, термически более стойких, чем простые комплексы типа HemVn в чистых металлах, приводит к формированию более мелких пузырьков и меньшему газовому распуханию сплавовAdditional details
Additional titles
- Original title (Russian)
- Модел' развития газовой пористости при послерадиационных отжигах OTsTs и GTsK материалов, облученных ионами гелия
Publishing Information
- Journal Title
- Fizika i Khimiya Obrabotki Materialov
- Journal Issue
- no.1
- Journal Page Range
- p. 18-25
- ISSN
- 0015-3214
- CODEN
- FKOMAT
INIS
- Country of Publication
- Russian Federation
- Country of Input or Organization
- Russian Federation
- INIS RN
- 37073524
- Subject category
- S36: MATERIALS SCIENCE;
- Descriptors DEI
- ANNEALING; BCC LATTICES; CONCENTRATION RATIO; CRYSTAL DEFECTS; HELIUM IONS; ION IMPLANTATION; KEV RANGE 10-100; NICKEL BASE ALLOYS; PHYSICAL RADIATION EFFECTS; POROSITY; RADIATION DOSES; STEEL-CR18NI10TI; SWELLING; TEMPERATURE RANGE 0400-1000 K; VOIDS
- Descriptors DEC
- ALLOYS; AUSTENITIC STEELS; CARBON ADDITIONS; CHARGED PARTICLES; CHROMIUM ALLOYS; CHROMIUM-NICKEL STEELS; CORROSION RESISTANT ALLOYS; CRYSTAL LATTICES; CRYSTAL STRUCTURE; CUBIC LATTICES; DEFORMATION; DIMENSIONLESS NUMBERS; DOSES; ENERGY RANGE; HEAT RESISTANT MATERIALS; HEAT RESISTING ALLOYS; HEAT TREATMENTS; HIGH ALLOY STEELS; IONS; IRON ALLOYS; IRON BASE ALLOYS; KEV RANGE; MATERIALS; NICKEL ALLOYS; RADIATION EFFECTS; STAINLESS STEELS; STEELS; TEMPERATURE RANGE; TITANIUM ADDITIONS; TITANIUM ALLOYS; TRANSITION ELEMENT ALLOYS
Optional Information
- Notes
- 24 refs., 6 figs., 1 tab.