Study of rare earth elements as material for control rods

The properties of rare earth elements as the material for control rods were studied. The rare earth elements, especially europium oxide, has the nuclear property corresponding to boron carbide, and its neutron absorption process does not emit alpha particles. The elements produced as a result of neutron capture also have large capture cross sections. This paper presents survey report on the properties and nuclear properties of rare earth elements, and comparison with other materials. Preliminary experiment was performed to make the pellets of europium oxide, and is described in this paper. Because of large density, the crystal form to be made was monoclinic system. Europium hydroxide was decomposed at 10000C and 10-5 torr. The obtained powder was dipped into benzene, and dryed in the air at 4500C. This powder was pressed and sintered in the air for one hour at 15000C. The density of the obtained pellets was 97.0% of the theoretical density. The cross section of europium for fast neutron absorption is not yet accurately obtained, and is in the range between 4.65 and 8.5 barn for 151Eu(n,γ) reaction. Since chain absorption reaction is caused in Eu, the overall capability of neutron absorption is not much changed by the loss of original material due to absorption. The pellets of europium oxide may be handled in air, but must be kept in dry atmosphere. The reactions of europium oxide with various metals were also investigated. The characteristic behavior in case of irradiation depends on the amount of silicon contained, and it was very good if the amount was less than 0.03%. (Kato, T.)