Effect of Nd content on the magnetic properties and crystallographic alignment of Fe - Nd - B - Al sintered magnets

Creators

  • 1. Faculty of Materials Science and Engineering, Warsaw University of Technology, Narbutta85, 02-524Warszawa (Poland)
  • 2. Department of Engineering Materials, The University of Sheffield, Sheffield S1 4DU (United Kingdom)

Description

The magnetic properties and crystallographic alignment for Fe - Nd - B - Al magnets having different Nd contents were studied. It was found that higher Nd concentration (above 18 at.%) resulted in deterioration of the alignment. Also, extended ball milling of the powder particles resulted in poorer alignment of the grains in the final sintered magnet. This behavior was attributed to the cold welding of the small particles of the Fe14Nd2B phase by mechanically soft Nd-rich phase in the course of ball milling. copyright 1997 Materials Research Society

Additional details

Publishing Information

Journal Title
Journal of Materials Research
Journal Volume
12
Journal Issue
10
Journal Page Range
p. 2715-2718.
ISSN
0884-2914
CODEN
JMREEE

INIS

Country of Publication
United States
Country of Input or Organization
United States
INIS RN
29021294
Subject category
S36: MATERIALS SCIENCE;
Descriptors DEI
ALUMINIUM COMPOUNDS; BORON COMPOUNDS; CERAMICS; IRON COMPOUNDS; MAGNETIC MATERIALS; MAGNETIC PROPERTIES; NEODYMIUM COMPOUNDS; SINTERING
Descriptors DEC
FABRICATION; MATERIALS; PHYSICAL PROPERTIES; RARE EARTH COMPOUNDS; TRANSITION ELEMENT COMPOUNDS