Emission of thermally stimulated luminescence in mixed monocrystals KCl-KBr: Pb2+, KCl: Pb2+ and KBr: Pb2+ exposed at low doses

It is reported the behavior of solid solutions of mixed crystals KCl1-x KBrx doped with divalent lead which were exposed to gamma radiation. The mixtures of KCl-KBr were varied, with x equivalents at 2, 50, 65, and 85 % including the extremes KCl: Pb2+ and KBr: Pb2+. It was maintained a concentration of divalent lead between 20 and 40 ppm in the crystalline lattice. The production of the generated defects by radiation have been correlated with the increase in the brilliance curves depending on the received dose by the mixed doped crystal. It has been used the thermal stimulation (Tl) for obtaining the crystal luminescence depending on the dose until 130 Gy with gammas of cobalt 60. The results shows that this mixed crystalline material of varied composition responds adequately to low doses which indicates that this would be a good detector of ionizing radiation. The results have been correlated with the optical properties of this mixed doped crystal, however it has been found that exists an important loss of luminescence depending on the halogen quantity presents in the mixed crystal. (Author)