Irradiation effect on PP/PMMA and PP/PP-g-PMMA matrices

The effects of PMMA and PP-g-PMMA on the oxidation of polypropylene (PP) have been studied. The mixing was done in Laboplastomill at the temperature of 200 oC, and screw speed of 20 rpm, for 5 minutes. The PMMA concentrations were 1, 2, 5, and 10% by weight, and PP-g-PMMA (12% grafting) 5, 10, and 20% by weight. Mechanical properties (tensile strength (Tb) and elongation at break (Eb)( of the mixture decreased with the increase of PMMA content over 5%. The addition of PMMA over 3% produced non-transparent film. Electron beam irradiation at the dose of 5, 10, 30, and 50 kGy was carried out to accelerate the matrix oxidation is accelerated. The optimum properties of PP/PMMA blends can be achieved by addition of maximum 2% PMMA either direct as PMMA or as compatibilizer (PP-g-PMMA). (authors)