Autowave deformation of single crystals of alloyed austenite
Creators
- 1. Inst. Fiziki Prochnosti i Materialovedeniya SO RAN, Tomsk (Russian Federation)
Description
Using single crystals of austenitic chromium-nickel (Fe - 18 Cr - 12 Ni - 2 Mo) and manganese (Fe - 13 Mn) steels the localization of deformation on specimen tension is investigated. The single crystals are grown by Bridgman method. Tensile tests are performed at 300 K and strain rate of 1.7 x 10-6 m/s. It is established that the deformation runs in a localized manner beginning from the yield stress to fracture. The dependences of curve shapes for plastic flow and strain localization on tension axis orientation and chemical composition of specimens are studied. The dependence of the velocity of localized plasticity auto wave propagation on the strain hardening factor at the linear stage is determined
Abstract (Russian)
На монокристаллах аустенитной хромоникелевой (Fe - 18 Cr - 12 Ni - 2 Mo) и марганцовистой (Fe - 13 Mn) сталей исследована локализация деформации при растяжении образцов. Монокристаллы сталей выращены по методу Бриджмена. Испытания на растяжение проводили при 300 К и скорости деформации 1.7 x 10-6 м/с. Установлено, что деформация протекает локализованно от предела текучести до разрушения. Исследованы зависимости формы кривых пластического течения и локализации деформации от ориентации оси растяжения и химического состава образцов. Установлена зависимость скорости распространения автоволн локализованной пластичности от коэффициента деформационного упрочнения на линейной стадииAdditional details
Additional titles
- Original title (Russian)
- Автоволновая деформация монокристаллов легированного аустенита
Publishing Information
- Journal Title
- Izvestiya Vysshikh Uchebnykh Zavedenij. Chernaya Metallurgiya
- Journal Issue
- no.8
- Journal Page Range
- p. 65-69
- CODEN
- IVUMAX
INIS
- Country of Publication
- Russian Federation
- Country of Input or Organization
- Russian Federation
- INIS RN
- 35008537
- Subject category
- S36: MATERIALS SCIENCE;
- Descriptors DEI
- CHROMIUM-NICKEL-MOLYBDENUM STEELS; DEFORMATION; FLOW STRESS; MANGANESE STEELS; MONOCRYSTALS; ORIENTATION; PLASTICITY; STRAIN HARDENING; STRAIN RATE; TEMPERATURE RANGE 0273-0400 K; TIME DEPENDENCE; ULTIMATE STRENGTH; YIELD STRENGTH
- Descriptors DEC
- ALLOYS; CARBON ADDITIONS; CHROMIUM ALLOYS; CHROMIUM STEELS; CHROMIUM-MOLYBDENUM STEELS; CHROMIUM-NICKEL STEELS; CRYSTALS; HARDENING; HIGH ALLOY STEELS; IRON ALLOYS; IRON BASE ALLOYS; MANGANESE ALLOYS; MECHANICAL PROPERTIES; MOLYBDENUM ALLOYS; NICKEL ALLOYS; STAINLESS STEELS; STEELS; STRESSES; TEMPERATURE RANGE; TRANSITION ELEMENT ALLOYS
Optional Information
- Notes
- 17 refs., 3 figs., 1 tab.