Preparation and properties of high-Tc Bi-oxide superconductors

Bulk superconductors of Pb-doped Bi-oxide system (BSCCO) dominated with the high-Tc phase have the critical transition temperature, Tc of 110 K, and the upper critical fields, Hc2 of 140 T at OK and 60 T at 77 K. A highly dense and a highly oriented microstructure is obtained by inserting an intermediate uniaxial pressing process. The critical current density, Jc at 77 K in zero field, Jc (77K,OT) of some 5000 A/cm2 can be easily obtained by this process, and the field dependence of Jc is also improved. Flexible high-Tc BSCCO ribbons with a Jc (77K,Ot) of 1850 A/cm2 have been successfully prepared by the combined process of doctor blade casting, cold rolling and sintering. Aq-sheeted multifilamentary wires with 1330 filaments and tapes with 30 filaments have also been successfully fabricated and the 36-filament tape shows a Jc(77K,OT) of 1050 A/cm2. (Auth.). 7 refs.; 7 figs