Gamma prime shape changes during creep of a nickel-base superalloy

Changes in the shape of the gamma-prime phase in the single-crystal nickel base alloy NASAIR 100 during tensile and compressive creep have been investigated experimentally by Laue X-ray diffractometry. It is found that under tensile loading, gamma-prime changes from the initial cubic shape to plates perpendicular to the applied stress. This change occurs during primary creep at 1000 C, 148 MPa. Prolonged creep exposures result in a thickening of the gamma-prime plates that is similar to Ostwald ripening often observed in other superalloys during creep. Under compressive loading, two sets of gamma-prime plates parallel to the applied stress are formed. 18 references