The system LaPO4 - Ca3(PO4)2 - Ca2P2O7
Creators
- 1. Department of Inorganic Chemistry, Faculty of Engineering and Economics, Wroclaw University of Economics, Wroclaw (Poland)
Description
The phase diagram of the ternary system LaPO4 - Ca3(PO4)2 - Ca2P2O7 has been determined by x-ray and microscopic examinations. The system contains only one double phosphate Ca3La(PO4)3 which is formed at the 1:1 molar ratio LaPO4 - Ca3(PO4)2. (author)
Additional details
Publishing Information
- Journal Title
- Polish Journal of Chemistry
- Journal Volume
- 76
- Journal Issue
- 8
- Journal Page Range
- p. 1101-1104
- ISSN
- 0137-5083
INIS
- Country of Publication
- Poland
- Country of Input or Organization
- Poland
- INIS RN
- 35061769
- Subject category
- S36: MATERIALS SCIENCE;
- Descriptors DEI
- CALCIUM PHOSPHATES; DIFFERENTIAL THERMAL ANALYSIS; LANTHANUM PHOSPHATES; OPTICAL MICROSCOPY; PHASE DIAGRAMS; POWDERS; SOLID SOLUTIONS; X-RAY DIFFRACTION
- Descriptors DEC
- ALKALINE EARTH METAL COMPOUNDS; CALCIUM COMPOUNDS; COHERENT SCATTERING; DIAGRAMS; DIFFRACTION; DISPERSIONS; HOMOGENEOUS MIXTURES; INFORMATION; LANTHANUM COMPOUNDS; MICROSCOPY; MIXTURES; OXYGEN COMPOUNDS; PHOSPHATES; PHOSPHORUS COMPOUNDS; RARE EARTH COMPOUNDS; SCATTERING; SOLUTIONS; THERMAL ANALYSIS
Optional Information
- Notes
- 8 refs, 3 figs