Formation of sputtered Y-Ba-Cu-O superconducting thin film on metal substrate
Creators
- 1. Materials Research Lab., Fujikura Ltd., 1-5-1 Kiba, Koto-ku, Tokyo 135 (Japan)
Description
Y1Ba2Cu3O7-x superconducting composites have been prepared on metallic substrate by rf magnetron sputtering method. Buffer layer of thin SrTiO3 layer between superconducting film and the substrate was found to be effective to realize superconductivity. Preferable grain alignment of c-axis was also obtained. The critical current density at 77K was 2.2 x 103 A/cm2 with Tc at 83K, and it was found that the thicker films had the higher Jc values
Additional details
Publishing Information
- Publisher
- Materials Research Society.
- Imprint Place
- Pittsburgh, PA (United States)
- ISBN
- 1-55899-057-7
- Imprint Title
- High-temperature superconductors: Fundamental properties and novel materials processing
- Imprint Pagination
- 1322 p.
- Journal Page Range
- p. 1201-1204.
Conference
- Title
- Materials Research Society fall meeting.
- Dates
- 27 Nov - 2 Dec 1989.
- Place
- Boston, MA (United States).
INIS
- Country of Publication
- United States
- Country of Input or Organization
- United States
- INIS RN
- 23034667
- Subject category
- S36: MATERIALS SCIENCE; S36: MATERIALS SCIENCE;
- Resource subtype / Literary indicator
- Conference
- Descriptors DEI
- BARIUM OXIDES; BUFFERS; COPPER OXIDES; CRITICAL CURRENT; CURRENT DENSITY; FABRICATION; GRAIN ORIENTATION; LAYERS; MAGNETRONS; METALS; SPUTTERING; STRONTIUM OXIDES; SUBSTRATES; SUPERCONDUCTING COMPOSITES; SUPERCONDUCTING FILMS; THIN FILMS; TITANIUM OXIDES; TRANSITION TEMPERATURE; YTTRIUM OXIDES
- Descriptors DEC
- ALKALINE EARTH METAL COMPOUNDS; BARIUM COMPOUNDS; CHALCOGENIDES; COMPOSITE MATERIALS; COPPER COMPOUNDS; CRYSTAL STRUCTURE; CURRENTS; ELECTRIC CURRENTS; ELECTRON TUBES; ELECTRONIC EQUIPMENT; ELEMENTS; EQUIPMENT; FILMS; MATERIALS; MICROSTRUCTURE; MICROWAVE EQUIPMENT; MICROWAVE TUBES; ORIENTATION; OXIDES; OXYGEN COMPOUNDS; PHYSICAL PROPERTIES; STRONTIUM COMPOUNDS; THERMODYNAMIC PROPERTIES; TITANIUM COMPOUNDS; TRANSITION ELEMENT COMPOUNDS; YTTRIUM COMPOUNDS
Optional Information
- Secondary number(s)
- CONF-891119--.