Electroplex emission from bi-layer blue emitting organic materials

Electroluminescence (EL) and photoluminescence (PL) spectra of an electron donor, an (poly(N-vinylcarbazole) (PVK))/electron acceptor, and a (2-(4-biphenylyl)-5-(4-tert-butylphenyl)-1,3,4-oxadiazole (PBD)) bi-layer solid film are analysed. The EL emission peak has an apparent red-shift with the increase of driving voltage. There maybe exist an electroplex emission between the PVK and PBD interface under high electric field strength. According to their energy level, the electroplex emission peak should locate at 460 nm. There are great spectra overlapping between PVK emission and electroplex emission, and the ratio of electroplex emission intensity to exciton emission intensity (Ielectroplex/Iexciton) increases from 0.38 at 10 to 0.81 at 16 V. Therefore the measured emission peaks continuously shift from 410 nm at 10 V to 445 nm at 16 V