The optical and mechanical properties of PVA-Ag nanocomposite films

Highlights: • We prepared PVA -Ag composite films which used in different filed of applications. • The XRD results showed Ag nanoparticles entering the polymer PVA matrix. • Optical band gap as a result of doping has been found to be reduced significantly. • Young's modulus increases while the strain decreases due to increasing Ag content. -- Abstract: Poly (vinyl alcohol) (PVA) loaded silver (Ag) nanoparticles were successfully prepared by chemical reduction methods. The synthesized nanoparticles are characterized using UV–visible spectrophotometer, X-ray diffractometer (XRD) and Transmission electron microscope (TEM). The contents of the inorganic phase in the nanocomposites were determined by using atomic absorption spectroscopy (AA) for silver, and were found to be 0.2, 0.4, 0.8 and 1.5 wt.%. Optical absorption studies in the wavelength range 190–900 nm showed additional peak at 420 nm for differently doped films, in addition to the peak at 200 nm for undoped PVA film. There is observable change in the absorbed intensity at 420 nm with filling levels. This is due to the link between the Ag metal ion and the polymer OH- groups. The indirect energy gaps were calculated. It was found that Young's modulus and the strength at the break increase, while the energy gaps and the strain decrease as the concentration of Ag content is increased. The XRD results showed that the Ag nanoparticles entering the polymer PVA matrix and the crystallinity was strongly influenced by the amount of Ag nanoparticles. The electron diffraction image for the highest concentration sample shows the crystalline nature of the silver metal nanoparticles. TEM of the nanocomposite films revealed the presence of Ag particles with average diameter of 12 nm