Preparation and characterization of a novel luminescent nanoparticles

In this paper, a new kind of fluorescent nanomaterial with morin modified alumina core and silica shell was prepared. Samples were characterized by transmission electron microscope (TEM), X-ray diffraction (XRD), Fourier transform infrared spectra (FT-IR), photoluminescent (PL) spectroscopy and fluorescence microscope. TEM results indicated that this material could be synthesized in nanometer range. PL spectra suggested that this new synthesized material was photostable and it showed nearly no dye leakage. This was because the dye molecules could form stable complex with the reactive aluminum cations on the surfaces of the alumina particles. The excitation and emission maxima of this new luminescent material were located at 420 and 493 nm, respectively. This new kind of luminescent nanomaterial was prepared by morin, AlCl3 and tetraethyl orthosilicate, which was very important for the large-scale and economic preparation luminescent nanoparticles because these precursors were inexpensive and the preparation process was convenient.