Super-tough poly(butylene terephthalate) based blends by modification with core-shell structured polyacrylic nanoparticles

Highlights: • We report a new method of synthesis of CSPN modifier. • The CSPN modifier was used to modify PBT and toughening effect was significant. • The highest notched impact strength of PBT/CSPN blend was 8.61 times greater than that of pure PBT. • The CSPN modifier and PBT/CSPN blend may offer new technology and great business opportunities. - Abstract: Core-shell structured polyacrylic nanoparticles (named CSPN) impact modifiers consisting of a rubbery poly(n-butyl acrylate) core and a rigid poly(methyl methacrylate) shell with a size of about 352 nm were synthesized by seed emulsion polymerization. The CSPN modifier with core-shell weight ratio 80/20 was used to toughen poly(butylene terephthalate) (PBT) by melt blending. With an increase in CSPN content, the impact strength and the elongation at break of PBT/CSPN blends increased significantly compared with those of PBT; however, the tensile strength decreased. It was found that the polymerization had a very high instantaneous conversion (> 93%) and overall conversion (99%). The core-shell structure of CSPN was examined by means of transmission electron microscope. Scanning electron microscope was used to observe the morphology of CSPN particle and fractured surfaces of the blends. The dynamic mechanical analyses of PBT/CSPN blends showed two merged transition peaks of PBT matrix, with the presence of CSPN modifier, which was responsible for the improvement of PBT toughness. The results indicated that the notched impact strength of PBT/CSPN blend with a weight ratio of 80/20 was 8.61 times greater than that of pure PBT where the brittle-ductile transition point appeared.