Free radicals trapped in polyethylene matrix

Two types of alkyl radicals were found to be trapped in irradiated crystals grown from polyethylene solution. One of them corresponds to the broad sextet pattern of the e.s.r. spectrum and the other corresponds to the sharp sextet pattern. The free radicals attributed to the broad sextet began to disappear at a lower temperature than the temperature at which the free radicals attributed to the sharp sextet disappeared. When butadiene molecules were brought into contact with the specimen, the decay of the free radicals corresponding to the broad sextet was accelerated. When the specimen was subjected to fuming nitric acid treatment, no broad sextet was observed. The mat of the crystals was aligned so that the c-axes of its crystallites were perpendicular to its surface. The broad sextet showed no anisotropy when the angle between the direction of applied magnetic field and that of the c-axis of the crystallite was varied. On the other hand, the sharp component of the spectrum showed apparent anisotropy. It can be concluded that the broad component comes from the free radicals trapped in the lamellar surface and the sharp component is attributed to the free radicals trapped in the inner part of the crystallite. (author)