In-situ graft-crosslinked gold nanoparticles with high-density surface defects and coated with a polytaurine membrane for the voltammetric determination of dopamine

Well-dispersed and graft-crosslinked gold nanoparticles (AuNPs) were synthesized by the reduction of tetrachloroaurate with hydrazine at room temperature. The AuNPs possess a high density of surface defects which is due to grafting of n-octanoic acid to polyvinylpyrrolidone. The physical and chemical properties of the resulting AuNPs were characterized by UV-vis, XRD, TEM/HRTEM, SAED, and XPS, respectively. The modified AuNPs were placed on a glassy carbon electrode (GCE) in an electropolymerized taurine layer to obtain a sensitive, selective, stable and rapid electrochemical dopamine sensor. The peak current, typically measured at 0.17 V (vs. SCE), increases linearly in the 1.0 to 120 μM dopamine concentration range, and the limit of detection (at S/N = 3) is 0.16 μM with a sensitivity of 2.94 μA·μM⁻¹·cm⁻². The sensor was successfully applied to the determination of dopamine in injections and spiked serum samples. The recoveries from spiked serum samples range from 97.5 to 102.4%, with RSDs ranging between 2.8 and 3.4%.

.