Development of Fuel Elements for the Thorium High Temperature Reactor (THTR). Results of the work carried out on behalf of the KFA between 1.4. to 30.6.1968. Quarterly Report No. 2/68
Description
Automatic translation: With the exception of the furnace line, the emulsion process was reduced to one Throughput for approx. 5 kg of heavy metal cut out per day. To improve the spherical shape of the cores, the washing plant will be modified to be necessary. Difficulties arising from organic contamination of thorium nitrate could be overcome. The high susceptibility to breakage of UO2 cores during drying and Sintering was significantly reduced by using isopropanol instead of carbon tetrachloride in the wash. The sintered particles had a geometric density of 72 to 86% in theory, a C content of 18-50 ppm and an O/U ratio from 2.00 - 2.01. Difficulties in coating UO2 cores led to Establishment of a coating temperature program, according to which fragmentless UO2 cores of size 500 - 4-500μ practically none Diffusion of heavy metal and without agglomeration with the desired layers can be provided. For the reactor test TD 5, sample WO 468f was prepared with emulsion cores, for the reactor test TD 4- prototype batches are running.
Abstract (German)
Das Emulsionsverfahren wurde mit Ausnahme der Ofenlinie auf einen Durchsatz für ca. 5 kg Schwermetall pro Tag ausgehaut. Zur Verbesserung der Kugelform der Kerne wird ein Umbau der Waschanlage notwendig sein. Schwierigkeiten, die von einer organischen Verunreinigung des Thoriumnitrats herrührten, konnten überwunden werden. Die hohe Bruchanfälligkeit von UO2-Kemen beim Trocknen und Sintern wurde erheblich verringert durch Verwendung von Isopropanol anstelle von Tetrachlorkohlenstoff beim Waschen. Die gesinterten Partikeln hatten eine geometrische Dichte von 72 bis 86% der Theorie, einen C-Gehalt von 18-50 ppm und ein O/U-Verhältnis von 2,00 - 2,01. Schwierigkeiten bei der Beschichtung von UO2-Kernen führten zur Aufstellung eines Beschichtungs-Temperaturprogrammes, nach dem bruchstückfreie UO2-Kerne der Größe 500 - 4-500μ praktisch ohne Diffusion von Schwermetall und ohne Zusammenballungen mit den gewünschten Schichten versehen werden können. Für den Reaktortest TD 5 wurde die Probe WO 468f mit Emulsionskernen hergestellt, für den Reaktortest TD 4- laufen Prototypchargen.
Files
Restricted
The record is publicly accessible, but files are restricted to users with access.
Additional details
Additional titles
- Original title (German)
- Entwicklung von Brennelementen für den Thorium Hochtemperatur Reaktor (THTR). Ergebnis der im Auftrag der KFA in der Zeit vom 1.4. bis 30.6.1968 durchgeführten Arbeiten. Vierteljahresbericht Nr. 2/68
Publishing Information
- Imprint Pagination
- 30 p.
- Report number
- INIS-DE--22M0162
INIS
- Country of Publication
- Germany
- Country of Input or Organization
- International Atomic Energy Agency (IAEA)
- INIS RN
- 53056983
- Subject category
- S21: SPECIFIC NUCLEAR REACTORS AND ASSOCIATED PLANTS;
- Descriptors DEI
- AGGLOMERATION; CARBON TETRACHLORIDE; DENSITY; EMULSIONS; FEDERAL REPUBLIC OF GERMANY; FORSCHUNGSZENTRUM JUELICH; FUEL ELEMENTS; HEAVY METALS; HTGR TYPE REACTORS; PERFORMANCE; PROPANOLS; TEMPERATURE RANGE 0400-1000 K; THORIUM; THORIUM NITRATES; URANIUM DIOXIDE
- Descriptors DEC
- ACTINIDE COMPOUNDS; ACTINIDES; ALCOHOLS; CHALCOGENIDES; CHLORINATED ALIPHATIC HYDROCARBONS; COLLOIDS; DEVELOPED COUNTRIES; DISPERSIONS; ELEMENTS; EUROPE; GAS COOLED REACTORS; GERMAN FR ORGANIZATIONS; GRAPHITE MODERATED REACTORS; HALOGENATED ALIPHATIC HYDROCARBONS; HYDROXY COMPOUNDS; METALS; NATIONAL ORGANIZATIONS; NITRATES; NITROGEN COMPOUNDS; ORGANIC CHLORINE COMPOUNDS; ORGANIC COMPOUNDS; ORGANIC HALOGEN COMPOUNDS; OXIDES; OXYGEN COMPOUNDS; PHYSICAL PROPERTIES; REACTOR COMPONENTS; REACTORS; TEMPERATURE RANGE; THORIUM COMPOUNDS; URANIUM COMPOUNDS; URANIUM OXIDES; WESTERN EUROPE
Optional Information
- Notes
- Document from Juelich Preservation Project; Figs., tabs.