Influence of initial magnetic state on the mode of field dependences of magnet hysteresis properties

Creators

  • 1. Tekhnicheskij Univ., Vena (Austria)
  • 2. Moskovskij Gosudarstvennyj Inst. Stali i Splavov, Moscow (Russian Federation)

Description

The specimens of sintered permanent magnets of alloy Nd2Fe14B doped with Dy, Tb and Al are used to measure coercive force, magnetization and remanent magnetization depending on a magnetizing field intensity for various initial states, namely, cyclically demagnetized, demagnetized by a negative field and thermally demagnetized ones. It is established that because of the influence of initial magnetic state on the course of field curves of magnetic properties it is recommended that all measurements are performed from a thermally demagnetized state when studying the mechanism of magnetic reversal in permanent magnets

Abstract (Russian)

На образцах спеченных постоянных магнитов из сплава Nd2Fe14B с добавками Dy, Tb и Al проведены измерения коэрцитивной силы, намагниченности и остаточной намагниченности в зависимости от величины намагничивающего поля для различных исходных состояний: циклически размагниченного, размагниченного отрицательным полем и термически размагниченного. Установлено, что из-за влияния исходного магнитного состояния на ход полевых зависимостей магнитных свойств при исследовании механизма перемагничивания в постоянных магнитах следует все измерения проводить из термически размагниченного состояния

Additional details

Additional titles

Original title (Russian)
Влияние исходного магнитного состояния на ход полевых зависимостей гистерезисных свойств магнита

Publishing Information

Journal Title
Izvestiya Vysshikh Uchebnykh Zavedenij. Chernaya Metallurgiya
Journal Issue
no.3
Journal Page Range
p. 49-50
CODEN
IVUMAX

INIS

Country of Publication
Russian Federation
Country of Input or Organization
Russian Federation
INIS RN
34014578
Subject category
S36: MATERIALS SCIENCE;
Descriptors DEI
ALUMINIUM ADDITIONS; BORON ALLOYS; COERCIVE FORCE; DYSPROSIUM ADDITIONS; HEATING; HYSTERESIS; IRON BASE ALLOYS; MAGNETIC FIELDS; MAGNETIZATION; NEODYMIUM ALLOYS; PERMANENT MAGNETS; SINTERED MATERIALS; TERBIUM ADDITIONS
Descriptors DEC
ALLOYS; ALUMINIUM ALLOYS; DYSPROSIUM ALLOYS; EQUIPMENT; IRON ALLOYS; MAGNETS; MATERIALS; RARE EARTH ADDITIONS; RARE EARTH ALLOYS; TERBIUM ALLOYS; TRANSITION ELEMENT ALLOYS

Optional Information

Notes
4 refs.; 2 figs.