Development of Corrosion Resistant Coating Systems for Molten Salt
Creators
- 1. Chungnam National University, Daejeon (Korea, Republic of)
Description
Several plasma sprayed ceramic coating systems were subjected to corrosion test. Among them, YSZ with functionally graded coating was found to be most durable in electrolytic reduction environment. The YSZ and Mg-Zr-O coatings, incorporating with four-layer functional gradient coating have been applied onto inner wall of metallic crucible, and the corrosion resistance of ceramic coated metallic has been evaluated in LiCl-Li2O molten salt at 650 .deg. C
Availability note (English)
Also available from KAERIFiles
42012359.pdf
Files
(2.0 MB)
| Name | Size | Download all |
|---|---|---|
|
md5:ee4197dfd5e8ee4923df1f3d0e1d8686
|
2.0 MB | Preview Download |
Additional details
Publishing Information
- Imprint Pagination
- 54 p.
- Report number
- KAERI/CM--1335/2008
INIS
- Country of Publication
- Korea, Republic of
- Country of Input or Organization
- Korea, Republic of
- INIS RN
- 42012359
- Subject category
- S36: MATERIALS SCIENCE;
- Descriptors DEI
- CERAMICS; COATINGS; CORROSION RESISTANCE; LITHIUM CHLORIDES; MOLTEN SALTS; PLASMA; REDUCTION
- Descriptors DEC
- ALKALI METAL COMPOUNDS; CHEMICAL REACTIONS; CHLORIDES; CHLORINE COMPOUNDS; HALIDES; HALOGEN COMPOUNDS; LITHIUM COMPOUNDS; LITHIUM HALIDES; SALTS
Optional Information
- Notes
- 15 refs, 29 figs, 3 tabs