Kinetics of growing the disordered antiphase domains in titanium carbohydride TiC0.50H0.21

For establishing formation and growth laws of the disordered nanostructures (the antiphase domains) in the nonstoichiometric titanium carbohydride with cubic NaCl type structure we quenched the titanium carbohydride TiC0.50H0.21 from 1000 deg C followed by annealing at 500, 600, 700, 800 deg C with 24 hour ageing. Neutron diffraction patterns were recorded after each annealing temperature. The half-width of the superstructure (111) reflection is shown to decrease with increasing the annealing temperature that testified on the disordered nanostructure size growing with temperature. The sizes of the disordered nanostructure formed at various temperatures and their dependence D = f(T) were determined on the basis of the neutron diffraction data. (authors)