Performance of magnetorheological elastomer based green epoxidized natural rubber/sucrose acetate isobutyrate hybrid matrix

This study introduces a sucrose acetate isobutyrate (SAIB) as a novel additive of magnetorheological elastomers (MREs). The MREs utilized an epoxidized natural rubber (ENR) as the matrix and carbonyl iron particles (CIPs) as their filler. The CIPs were fixed at 60 wt%. The viscosity of the compound was observed using a viscometer. Meanwhile, the microstructures were observed by using field emission scanning electron microscope (FESEM). Rheological properties regarding shear storage modulus were measured by using a rheometer (MCR 302, Anton Paar). The experimental results demonstrated that the MREs-based ENR/SAIB had a decrement in their viscosity by 40% reduction. Moreover, the magnetorheological (MR) effect increased by 23% as the increment of magnetic fields. The morphological photograph showed that the CIPs embedded well within the matrix. The fabricated MREs samples were strain dependent, where all MREs samples exhibit the deteriorating trend when increasing the strain amplitude. (paper)