Influence of Selective Laser Melting Processing Parameters of Co-Cr-W Powders on the Roughness of Exterior Surfaces

Selective Laser Melting (SLM) represents an Additive Manufacturing method widely used in medical practice, mainly in dental medicine. The powder of 59% Co, 25% Cr, 2.5% W alloy (Starbond CoS Powder 55, S&S Scheftner C, Germany) was processed (SLM) on a Realizer SLM 50 device (SLM Solution, Germany). After laser processing and simple sanding with Al₂O₃ or two-phase sanding (Al₂O₃ and glass balls), measurements of surface roughness were conducted. This paper presents the influences exercised by laser power (P = 60 W, 80 W and 100 W), the scanning speed (vscan = 333 mm/s, 500 mm/s and 1000 mm/s) and exposure time (te = 20 µs, 40 µs and 60 µs) on the roughness of surfaces obtained by SLM processing. Based on the experimental results obtained for roughness (Ra), some recommendations regarding the choice of favorable combinations among the values of technological parameters under study in order to obtain the surface quality necessary for subsequent applications of the processed parts (SLM) have been made. (paper)