On the influence of the material toughness and the state of stress on fracture of large scale specimens

Creators

  • 1. Stuttgart Univ. (Germany, F.R.). Staatliche Materialpruefungsanstalt

Description

The results obtained with the SENT samples (20 MnMoNi 55 (USA) and 22 NiMoCr 37 (KS07)) show the analysis of the multi-axis degrees of stress condition to be an important tool in the fracture-mechanics description of the failure course. Results suggest that sample failure will begin in the minimum of the multi-axis ratio. This minimum is locally restricted to the notch bottom; hence, study results gained to date suggest stable crack growth. However, if there is a continuously high multi-axis degree in the ligament, sample failure without previous stable crack growth will have to be reckoned with. (orig./DG)

Abstract (German)

Die Ergebnisse an den SENT-Proben 20 MnMoNi 55 (KS17) und 22 NiMoCr 37 (KS07) zeigen, dass fuer die bruchmechanische Beschreibung des Versagensablaufes die Analyse des Mehrachsigkeitsgrades des Spannungszustandes ein wichtiges Hilfsmittel darstellt. Der Schluss liegt nahe, dass das Probenversagen dort beginnt, wo das Minimum des Mehrachsigkeitsquotienten auftritt. Ist das Minimum oertlich sehr eng auf den Kerbgrund begrenzt, so kann nach den bisherigen Versuchsergebnissen mit stabilem Risswachstum gerechnet werden. Liegt jedoch ein konstant hoher Mehrachsigkeitsgrad im Ligament vor, muss mit einem Probenversagen ohne vorhergehendes, stabiles Risswachstum gerechnet werden. (orig./DG)

Additional details

Additional titles

Original title (German)
Einfluss der Werkstoffzaehigkeit und des Spannungszustandes auf das Versagensverhalten von Grossproben

Publishing Information

Imprint Title
Safety and reliability of pressure components with special emphasis on advanced methods of NDT. Vol. 2
Imprint Pagination
325 p.
Journal Page Range
p. 30.1-30.24.
Report number
INIS-mf--11897

Conference

Title
12. MPA seminar on safety and reliability of pressure components with special emphasis on advanced methods of NDT.
Dates
9-10 Oct 1986.
Place
Stuttgart (Germany, F.R.).

INIS

Country of Publication
Germany
Country of Input or Organization
Germany
INIS RN
20028941
Subject category
S36: MATERIALS SCIENCE; S22: GENERAL STUDIES OF NUCLEAR REACTORS;
Resource subtype / Literary indicator
Conference
Descriptors DEI
CHARPY TEST; CRACK PROPAGATION; DEFORMATION; FRACTURE MECHANICS; REACTOR COMPONENTS; S-N DIAGRAM; STEELS; STRESS ANALYSIS
Descriptors DEC
ALLOYS; CARBON ADDITIONS; DESTRUCTIVE TESTING; DIAGRAMS; IMPACT TESTS; INFORMATION; IRON ALLOYS; IRON BASE ALLOYS; MATERIALS TESTING; MECHANICAL TESTS; MECHANICS; TESTING

Optional Information

Notes
Imprint:Sicherheit und Verfuegbarkeit in der Anlagentechnik mit dem Schwerpunkt Fortgeschrittene ZFP-Methoden. Bd. 2.;Festigkeit und Sicherheit.