Thermoluminescence analysis of co-doped NaCl at low temperature irradiations

The thermoluminescent response and kinetics parameters of NaCl, doubly activated by Ca-Mn and Cd-Mn ions, exposed to gamma radiation are analyzed. The doped NaCl samples were irradiated at relative low temperature, i.e. at the liquid nitrogen temperature (LNT) and at dry ice temperature (DIT), and the glow curves obtained after 2 Gy of gamma irradiation were analyzed using the computerized glow curve deconvolution (CGCD). An evident variation in the glow curve structure after LNT and DIT was observed. It seems that different kinds of trapping levels are activated at relative low temperature. The original two prominent peaks in compositions A (Ca,Mn) and B (Ca,Mn) have been changed in only one main peak with satellites in the low temperature side of the glow curves. In compositions C (Cd,Mn) and D (Cd,Mn), low temperature peaks become stronger and prominent than the high temperature peaks; this effect could be explained considering that the trapping probability for low temperature traps, the one very close to the conduction band, is enhanced by low temperatures during irradiation.