Welding and fracture mechanics experiments in pieces and components of X 20 CrMoV 12 1 with wall thicknesses up to 270 mm
Description
The findings of these experiments help to find out whether and how safe operation of containers etc. is possible at these wall thicknesses at the present minimum toughness values or whether the toughness of base metal and welding deposits requires improvement. For this purpose, a weldless pipe with a clear opening of 600 mm and a wall thickness of 95 mm was provided with a longitudinal and a circumferential weld and with defined faults, and the crack growth behaviour with increasing internal pressure as well as the burst behaviour was investigated. The longitudinal weld was made in order to account for a possible development towards longitudinally welded components. Comparative and supplementary analyses were carried out on forged plates with thicknesses of 100 and 270 mm in order to be able to make statements also for these thickness ranges. (orig./IHOE)
Abstract (German)
Die Ergebnisse und Erfahrungen der durchgefuehrten Untersuchungen sind ein Beitrag zur Klaerung der Frage, ob und wie bei den betrachteten Wanddicken mit den derzeit gueltigen Mindestzaehigkeitswerten ein sicherer Betrieb von Behaeltern u.ae. gewaehrleistet ist bzw. ob im Grundwerkstoff und im Schweissgut Verbesserungen der Zaehigkeit erforderlich sind. An einem nahtlosen Schuss 600 li Durchmesser x 95 mm Wanddicke mit spaeter eingebrachter Laengs- und Rundnaht und definierten kuenstlichen Fehlerstellen wurde das Risswachstumsverhalten bei schwellendem Innendruck sowie anschliessend das Berstverhalten untersucht. Neben der Rundnaht wurde zusaetzlich eine Laengsnaht gelegt, um auch moeglichen Entwicklungen zu laengsgeschweissten Bauteilen Rechnung zu tragen. Vergleichende und ergaenzende Untersuchungen wurden an 100 und 270 mm dicken geschmiedeten Platten mit Schweissnaehten durchgefuehrt, um auch Aussagen fuer Wanddicken von 100 bis 270 mm machen zu koennen. (orig./IHOE)Additional details
Additional titles
- Original title (German)
- Schweiss- und Bruchmechanikversuche an Proben und Bauteilen aus Werkstoff X 20 CrMoV 12 1 bei Wanddicken bis 270 mm
- Augmented title (English)
- German material no. 1.4922
Publishing Information
- Journal Title
- VGB Kraftwerkstech.
- Journal Volume
- 60
- Journal Issue
- 4
- Series
- VGB Kraftwerkstech.
- Journal Page Range
- 305-319
- ISSN
- 0372-5715
INIS
- Country of Publication
- Germany
- Country of Input or Organization
- Germany
- INIS RN
- 11562510
- Subject category
- S42: ENGINEERING; S36: MATERIALS SCIENCE; S22: GENERAL STUDIES OF NUCLEAR REACTORS;
- Is Lead record
- Yes
- Descriptors DEI
- BOILERS; BRINELL HARDNESS; CHEMICAL COMPOSITION; CHROMIUM-MOLYBDENUM STEELS; CONTAINERS; CRACK PROPAGATION; CRACKS; DEPOSITS; DUCTILITY; EMBRITTLEMENT; FAILURES; FATIGUE; FRACTURE MECHANICS; HEAT AFFECTED ZONE; HEAT RESISTING ALLOYS; HEAT TREATMENTS; IMPACT TESTS; NOTCHES; PERFORMANCE TESTING; PIPES; PLATES; PRESSURE DEPENDENCE; RESEARCH PROGRAMS; RESIDUAL STRESSES; SPECIFICATIONS; STRAINS; STRESS INTENSITY FACTORS; STRESS RELAXATION; TEMPERATURE DEPENDENCE; THICKNESS; TIME DEPENDENCE; VANADIUM ALLOYS; WELDED JOINTS; WELDING
- Descriptors DEC
- ALLOYS; CARBON ADDITIONS; CHROMIUM ALLOYS; CHROMIUM STEELS; DIMENSIONS; FABRICATION; IRON ALLOYS; IRON BASE ALLOYS; JOINING; JOINTS; MATERIALS TESTING; MECHANICAL PROPERTIES; MECHANICAL TESTS; MECHANICS; MOLYBDENUM ALLOYS; STEELS; STRESSES; TENSILE PROPERTIES; TESTING; TRANSITION ELEMENT ALLOYS