Irradiation effects on reactor structural materials. Semi-annual progress report, August 1974--February 1975

Data are reported on: effects of cold work on creep-fatigue of irradiated 304 and 316 stainless steel (ss); swelling of 304 and 316 ss irradiated with protons and fast neutrons; effects of hold time on fatigue crack propagation in neutron-irradiated 20 percent cold-worked 316 ss; radiation resistance of 0.03 percent Cu A533-B steel; microstructure of irradiated Inconel 718, Incoloy 800, PH13-8Mo, Mo, and Nb; dose dependence of 2.8-MeV Ni+ ion damage (swelling) in Ni; notch ductility and strength of 316 ss submerged arc weld deposits; effects of microstructure of 316 ss on its irradiation response; in-reactor deformation of 20 percent cold-worked 316 ss; microstructure of HFIR-irradiated 316 ss; void microstructures of V bombarded by 46-MeV Ni6+ ions (with and without preinjected helium) or 7.5-MeV Ta3+ ions; swelling of Mo, Mo--0.5 Ti, Nb, Nb--1 Zr, W, and W--25 Re after fast neutron irradiation; swelling of V ion-irradiated Mo; creep of 20 percent cold-worked 316 ss at 850, 1000, and 11000F; effects of fast neutrons on mechanical properties of 20 percent cold-worked 316 ss; notch effects in tensile behavior of irradiated, annealed 304 ss (EBR-II duct thimbles); equations for thermal creep in pressurized tubes of 20 percent cold-worked 316 ss; irradiation creep in cold-worked 316 ss; helium production cross sections in neutron-irradiated elements; and radiation effects on various alloys. (U.S.)