Synthesis of ZnS thin films from aqueous caustic of trisodium citrate and their properties

Zinc sulfide (ZnS) thin films due to their properties are widely used in various electronic optical devices. They are produced by several methods, among which - vacuum sublimation, high frequency sputtering method, quasiclosed volume method, sol-gel method, electrodeposition. These methods have high energy consumption which increases the price of ZnS thin films. The aim of this work is to establish the optimal parameters of the synthesis of ZnS thin films of the aqueous caustic and the correlation between content of zinc in the synthesized films determined by the method of stripping voltammetry and thickness, structural, morphological and optical parameters. The ZnS thin films were obtained from aqueous caustics of zinc-containing salt using chemical deposition. Fresh solution of zinc-containing salt, trisodium citrate (Na₃C₆H₅O₇) as a complexing agent, thiourea ((NH₂)₂CS) and ammonium hydroxide (NH₄OH) was used for the synthesis of ZnS films by chemical deposition. The deposition was performed on prepared glass substrates with the area of 5,76 cm². The phase mixture of the films has been determined. It showed the presence of ZnS compounds in the cubic modification (sphalerite). Stripping voltammetry was used to determine the mass of zinc in the ZnS films on various conditions of synthesis, namely on the concentration of the initial zinc-containing salt, trisodium citrate, thiourea, deposition time and temperature. The surface morphology, optical properties, the thickness of the ZnS resulting films have been studied. The optimal conditions for the synthesis of ZnS films were found based on these data. Three-dimensional surface morphology of ZnS film studies showed its smoothness, uniformity, integrity and confirmed the correctness of determining the optimal synthesis parameters