Colloidal silver nanoparticle gradient layer prepared by drying between two walls of different wettability

A one-dimensional silver (Ag) nanoparticle gradient layer is prepared from an aqueous colloidal solution upon a polystyrene (PS) coated silicon (Si) substrate. For preparation two walls of different wettability are used. The 40 nm PS-layer exhibits a locally constant film thickness due to the strong roughness correlation with the underlying Si-substrate and is less wettable as compared to the glass plate placed above. The Ag nanoparticles have a triangular prism-like shape. The structural characterization of the obtained complex gradient formed by drying is performed with microbeam grazing incidence small-angle x-ray scattering based on compound refractive lenses. Due to the adsorption from aqueous solution in the selective geometry a double gradient type structure defined by two areas with characteristic lateral lengths and a cross-over regime between both is observed.