Benchmark Tests to Develop Analytical Time-Temperature Limit for HANA-6 Cladding for Compliance with New LOCA Criteria

According to 10CFR50.46c, two analytical time and temperature limits for breakaway oxidation and postquench ductility (PQD) should be determined by approved experimental procedure as described in NRC Regulatory Guide (RG) 1.222 and 1.223. According to RG 1.222 and 1.223, rigorous qualification requirements for test system are required, such as thermal and weight gain benchmarks. In order to meet these requirements, KEPCO NF has developed the new special facility to evaluate LOCA performance of zirconium alloy cladding. In this paper, qualification results for test facility and HT oxidation model for HANA-6 are summarized. The results of thermal benchmark tests of LOCA HT oxidation tester is summarized as follows. 1. The best estimate HT oxidation model of HANA- 6 was developed for the vender proprietary HT oxidation model. 2. In accordance with the RG 1.222 and 1.223, Benchmark tests were performed by using LOCA HT oxidation tester 3. The maximum axial and circumferential temperature difference are ± 9 .deg. C and ± 2 .deg. C at 1200 .deg. C, respectively. At the other temperature conditions, temperature difference is less than 1200 .deg. C result. Thermal benchmark test results meet the requirements of NRC RG 1.222 and 1.223